Degradation of Poly(lactic acid) under Simulated Landfill Conditions |
|---|---|
| รหัสดีโอไอ | |
| Creator | Chomnutcha Boonmee, Charnwit Kositanont and Thanawadee Leejarkpai |
| Title | Degradation of Poly(lactic acid) under Simulated Landfill Conditions |
| Publisher | Faculty of Environment and Resource Studies, Mahidol University |
| Publication Year | 2559 |
| Journal Title | Environment and Natural Resources Journal |
| Journal Vol. | 14 |
| Journal No. | 2 |
| Page no. | 1-9 |
| Keyword | Poly(lactic acid)/ PLA/ Degradation/ Physical Properties |
| ISSN | 1686-5456 |
| Abstract | In this study, the physical and chemical properties change of poly(lactic acid) after burying in the mixture of soil and sludge under thermophilic (61 ?C) oxygen limited conditions were investigated using various analytical techniques. The environmental factors under these setting conditions and microbial activities accelerated the degradation process of PLA. Under tested conditions, PLA loss their weight about 90% at the burying time of 90 days. During the degradation process, PLA samples were continuously broken to small fragile fragments and showed the size less than 1 mm at the end of degradation test. Change of the surface morphology change was revealed by scanning electron microscopy (SEM). Many pores, cracks and irregular roughness were presented on the PLA surface. Thermal decomposition was decreased from 387.8 to 289.2 ?C. The percentage of carbon content in molecular structure decreased from 49.46% to 45.42%. In addition, the Fourier transformed infrared spectroscopy (FTIR) revealed the change of ester bonds. This study can be used for developing PLA waste management process. |