Prevention of dealloying in manganese aluminium bronze propeller: Part II |
|---|---|
| รหัสดีโอไอ | |
| Creator | 1. Napachat Tareelap 2. Kaysinee Sriraksasin 3. Nakorn Srisukhumbowornchai 4. Swieng Thuanboon 5. Choochat Nitipanyawong |
| Title | Prevention of dealloying in manganese aluminium bronze propeller: Part II |
| Publisher | Faculty of Engineering, Khon Kaen Univeristy |
| Publication Year | 2557 |
| Journal Title | KKU Engineering Journal |
| Journal Vol. | 41 |
| Journal No. | 1 |
| Page no. | 83-90 |
| Keyword | Dealloying corrosion,Corrosion prevention,Cathodic protection,Manganese aluminium bronze (MAB), Sacrificial anode |
| ISSN | 0125-8273 |
| Abstract | Due to the failure of manganese aluminium bronze (MAB) propeller caused by dealloying corrosion as described in Part I [1], this work aims to study the prevention of dealloying corrosion using aluminium and zinc sacrificial anodes. The results indicated that both of the sacrificial anodes could prevent the propeller from dealloying. Moreover, the dealloying in seawater was less than that found in brackish water. It was possible that hydroxide ions, from cathodic reaction, reacted with calcium in seawater to form calcium carbonate film protecting the propeller from corrosion. |