Influence of amorphous silica in perlite on compressive strength and pozzolanic reaction of blended cement paste |
|---|---|
| รหัสดีโอไอ | |
| Creator | 1. Piyachat Suphawithayacharoenkun 2. Wunchock Kroehong 3. Threerawat Sinsiri |
| Title | Influence of amorphous silica in perlite on compressive strength and pozzolanic reaction of blended cement paste |
| Publisher | Faculty of Engineering, Khon Kaen Univeristy |
| Publication Year | 2555 |
| Journal Title | KKU Engineering Journal |
| Journal Vol. | 39 |
| Journal No. | 3 |
| Page no. | 257-266 |
| Keyword | Perlite X-ray, Diffraction, Analysis, Pozzolanic, Amorphous |
| ISSN | 0125-8573 |
| Abstract | This research was to determine the amorphous silica in perlitethat affected compressive strength and degree of pozzolanicreaction by using X-ray diffraction method. In this study, perlite was burnt at different temperaturesof 600?c, 700 ?c and 800?c and different timeof 4, 6 and 8 hr. Perlite and sand were ground to approximately the same finenessascement. Portland cement type1 was replaced by perlite or ground sand at 20% by weight of cementitiousmaterial. A water to binder ratio(w/c) of 0.40 was used. The result of X-ray diffraction showedthat the perlite burnedat 600?c for 4 hr. contained the largestamorphousesilica.From the compressive strength test and the pozzolanic activity testit was shownthat the amorphouse silica contents affected on compressive strength and degree of pozzolanic reaction |