Effect of pure titanium particle size on density, hardness, wear resistance and microstructure properties |
|---|---|
| รหัสดีโอไอ | |
| Creator | Tugba MUTUK |
| Title | Effect of pure titanium particle size on density, hardness, wear resistance and microstructure properties |
| Contributor | Mevl?t G?RB?Z |
| Publisher | Metallurgy and Materials Science Research Institute Chulalongkorn University |
| Publication Year | 2562 |
| Journal Title | Journal of Metals Materials and Minerals |
| Journal Vol. | 29 |
| Journal No. | 3 |
| Page no. | 54-59 |
| Keyword | Titanium, Particle size, Hardness, Wear resistance, Microstructure |
| URL Website | http://ojs.materialsconnex.com/index.php/jmmm/article/view/533 |
| Website title | Effect of pure titanium particle size on density, hardness, wear resistance and microstructure properties | Mutuk | Journal of Metals, Materials and Minerals |
| ISSN | 8576149 |
| Abstract | In this study, pure titanium particle samples with different particle sizes were produced by powder metallurgy method. In the sample production, pure titanium particles having a different particle size of ?30?m, ?43?m, ?150?m were used. Titanium (Ti) samples were sintered at 1100?C for 120 min. Density, hardness, wear resistance and microstructure analyzes were performed on the Titanium samples. According to the results, the best mechanical properties values were obtained with ?30 ?m particle size of Titanium. The best density and hardness results are 4.28 g?cm-3 and 419.8 HV, respectively. The results of the wear rate were found under 30 N load of 8.21?10-5 mm3?Nm. Mass loss results were measured as 5.2 mg (under load of 30 N). SEM analyses showed that a good bonding and strong neck formation between the particles were observed for particle size of ?30 ?m. |