รหัสดีโอไอ 10.14456/jmmm.2020.28
Creator Ekkarat CHUSONG
Title Dry-sliding wear of the 316L/h-BN composites produced under crack ammonia atmosphere
Contributor Panya KANSUWAN; Naoto OHTAKE; Pongsak WILA; Nattaya TOSANGTHUM; Ruangdaj TONGSRI
Publisher Metallurgy and Materials Science Research Institute Chulalongkorn University
Publication Year 2020
Journal Title Journal of Metals Materials and Minerals
Journal Vol. 30
Journal No. 2
Page no. 117-123
Keyword 316L stainless steel ,Hexagonal boron nitride ,Self-lubricating composite ,Hardness ,Dry-sliding wear
URL Website https://ojs.materialsconnex.com/index.php/jmmm/article/view/700
Website title Dry-sliding wear of the 316L/h-BN composites produced under crack ammonia atmosphere | Chusong | Journal of Metals, Materials and Minerals
ISSN 8576149
Abstract Wear is one of different problems in mechanical failures of moving components. When a component encounters friction force on its surface, crack initiation tends to occur and wear follows crack propagation. Thus, the moving parts of automobiles should have proper wear resistance for long-time services, in addition to having high strength and hardness for heavy load operation. A self-lubricating material with compromised tribological and mechanical properties is important for some moving components. In this work, self-lubricating composites, metal matrix composites embedded with a solid lubricant, made from 316L stainless steel powder mixed with different hexagonal boron nitride (h-BN) contents of 10%, 15% and 20% by volume. The mixed powders were compacted into green parts (according with MPIF Standard 42) with density of 6.5 gทcm-3. Then, the green parts were sintered at 1100, 1150, 1200, 1250 and 1300ฐC under cracked ammonia (75% H2+25% N2) atmosphere for 60 min. The experimental results revealed that increases of hardness and strength sintered 316L matrix by reduction of pore amount and size were due to the increase of sintering temperature. However, the increase of h-BN content resulted in increase of pore amount and size. Additions of h-BN content up to 20 vol. % reduced friction coefficient of the sintered composites. At sintering temperatures of equal to and higher than 1200ฐC, h-BN did not react with 316L stainless steel powders to form intergranular boride phase. The sintered composites produced under the maximum experimental sintering temperature of 1300ฐC showed low specific wear rate.
ดิจิตอลไฟล์ Digital File

บรรณานุกรม

Ekkarat CHUSONG,Panya KANSUWAN; Naoto OHTAKE; Pongsak WILA; Nattaya TOSANGTHUM; Ruangdaj TONGSRI. (2020) Dry-sliding wear of the 316L/h-BN composites produced under crack ammonia atmosphere. Journal of Metals Materials and Minerals,30,117-123.
Ekkarat CHUSONG,Panya KANSUWAN; Naoto OHTAKE; Pongsak WILA; Nattaya TOSANGTHUM; Ruangdaj TONGSRI. "Dry-sliding wear of the 316L/h-BN composites produced under crack ammonia atmosphere". Journal of Metals Materials and Minerals 30 (2020):117-123.
Ekkarat CHUSONG,Panya KANSUWAN; Naoto OHTAKE; Pongsak WILA; Nattaya TOSANGTHUM; Ruangdaj TONGSRI. Dry-sliding wear of the 316L/h-BN composites produced under crack ammonia atmosphere. Metallurgy and Materials Science Research Institute Chulalongkorn University:ม.ป.ท. 2020.